ASA-GF
Eryone ASA-GF is an easy-to-print 3D printing material characterized by high
strength, high rigidity, weather resistance, anti-yellowing, aging resistance, and
corrosion resistance. It is designed for easy shaping, with a low tendency to crack or
warp, and supports open printing environments. The printed parts are robust and
feature a matte, frosted surface texture. This material is ideal for applications requiring
specific strength or weather resistance in end-use products, such as automotive interior
components, garden furniture, and outdoor leisure structures. It contains 10% fiberglass.
Part I:Suggests Printing Parameters
| Parameter | Set up |
| Nozzle temperature | 260℃-280℃ |
| Bed temperature | 90-100℃ |
| Bed materia | glass, PEI, spring steel plate |
| Bottom printing temperature | 260℃-280℃ |
| Sealed printing | supports open printing, and the sealing effect is better if it is sealed |
| Printing speed | 30-150mm/s |
| Drying conditions | 80℃，4H |
Part II:Physical Properties of Materials
| Property | Testing Method | Unit | Typical Value |
| Density(g/cm³ at 21.5 ° C） | ASTM D792 (ISO 1183, GB/T 1033) | g/cm³ | 1.17 |
| Vicat Softening Temperature(° C) | ASTM D1525 (ISO 306 GB/T 1633) | ℃ | / |
| Heat distortion temperature(° C) | ASTM D648 1.8MPa 0.45MPa | ℃ | 86 |
| Glass transition temperature (° C) | DSC, 10 ° C/min | ℃ | 104 |
| Melt Index(g/10 min) | 220 ° C, 10kg 240 ° C, 2.16 kg | g/10min | 10 |
Part III:Mechanical Properties of Printed Samples
| Property | Test conditions | Test standards | unit | Typical Value |
| Tensile strength X-Y | 50mm/min | GB/T 1040.4 | MPa | 34.2 |
| Elastic modulus X-Y | 50mm/min | GB/T 1040.1-2006 | MPa | 1857.9 |
| Elongation at break X-Y | 50mm/min | GB/T 1040.4 | MPa | 4.3 |
| Tensile strength X-Z | 50mm/min | GB/T 1843 | MPa | 21.2 |
| Elastic modulus X-Z | 50mm/min | GB/T 1040.1-2006 | MPa | 1593.1 |
| Elongation at break X-Z | 50mm/min | GB/T 1040.4 | % | 2.1 |
| Bending strength | 2mm/min | GB/T 9341 | MPa | 54.3 |
| Bending modulus | 2mm/min | GB/T 9341 | MPa | 2623.5 |
| Charpy Impact strenght | 2.75J | GB/T 1043.1-2008 | kJ/m2 | 9.6 |
Note: All splines are printed under the following conditions: printing temperature=270 ° C, printing
speed=80mm/s, base plate 95 ° C, filling=100%, nozzle diameter=0.4mm